Pengaruh Jumlah Bahan Pengisi Terhadap Kekerasan Kompon Footstep Sepeda Motor
DOI:
https://doi.org/10.25181/prosemnas.v0i0.713Abstrak
One of the problems encountered at the time of manufacture of rubber finished goods is to determine precisely the value of hardness of rubber finished goods because hardness is one of the important physical properties in designing rubber finished goods. The hardness of rubber finished goods can be predicted before by considering some materials that contribute to the final hardness of rubber finished goods. The purpose of this study is to determine the effect of the amount of filler material to the hardness of footstep motorcycle compound. The experiment was carried out by experimenting with three compound formulas (F1, F2, and F3) using natural rubber and chemicals. The experimental compound will be compared to the manufactured product compound (FP) by analyzing the hardness value (Hardness, Shore A). The use of an increasing amount of filler will increase the hardness value of the compound. Keywords : filler, footstep, hardnessÂUnduhan
Referensi
Bonstra, B.B. 2005. Mixing of carbon black and polymer: interaction and reinforcement. Journal of Applied Polymer Science, 11 : 389-406.
CDM Training Centre. 2016. Bimbingan Teknis Manufaktur Produk Karet. Makalah Pelatihan barang Jadi Karet. Bandung.
Cipriadi, A. 2016. Pengetahuan Bahan untuk Pembuatan Produk Karet. Makalah Pelatihan Pembuatan Barang Jadi Karet. Balai Riset dan Standadisasi Industri Palembang.
Daud, D dan Suharman. 2016. Pemanfaatan Karet Limbah Industri Crumb Rubber Sebagai Substitusi Karet SIR Pada Pembuatan Suku Cadang Sepeda Motor. Prosiding Seminar Nasional Kulit, Karet dan Plastik Ke-5 ISSN : 2477-3298. Yogyakarta
Hendrawan, M.A., Purbputro, P.I. 2015. Studi karakteristik sifat mekanik kompon karet dengan variasi komposisi sulfur dan carbon black sebagai bahan dasar ban luar. Simposium Nasional Teknologi Terapan (SNTT) 3
Pusat Penelitian Karet Bogor. 2015. Makalah Kursus Teknologi Kompon Karet Padat, Sabut Kelapa Berkaret dan Lateks Pekat Serta Uji Mutu Karet. Bogor.
Rahmaniar, Rejo, A., Priyanto, G., Hamzah, B. 2014. Pemanfaatan tepung dari kulitsecang, kunyit dan kulit manggis untuk kompon karet. Jurnal Dinamika Penelitian Industri, 25(1): 71-78.
Rencana Pelaksanaan Program Pengembangan Pendidikan Politeknik Negeri. 2014. Politeknik Negeri Lampung.
Simpson, R.B. 2002. Rubber Basics, United Kingdom: Rapra Technology Ltd.
Supraptiningsih, Buchori, A., Lestari, S.B.P. 2005. Pengaruh RSS dan filler CaCO3 terhadap sifat fisis kompon karpet karet. Jurnal Kulit, Karet dan Plastik, 21(1): 34-40.